Howell
Fiberglass Thermal Insulation Tissue
Technical Data
Product Code | Unit Weight (g/m2) | LOI (%) | MD Tensile Strength (N/50mm) | CD Tensile Strength (N/50mm) | Thickness(mm) | Moisture Content (%) |
BW200 | 200 | 8.0 | ≥280 | ≥140 | 2.0 | ≤1.0 |
BW300 | 300 | 8.0 | ≥350 | ≥200 | 3.0 | ≤1.0 |
BW400 | 400 | 8.0 | ≥420 | ≥250 | 4.0 | ≤1.0 |
Testing Basis | ISO 3374 | ISO 1887 | ISO 3342 | ISO 3342 | ISO4603@0.5KPa | ISO 3344 |
Paper core diameter: 76/152mm
Remark:
1. Any special products can also supply according to customers' request
2. The technical data above is for reference only
Description
Fiberglass thermal insulation tissue is made of E chopped fiber glass with wet laid process and cured at high
temperature after impregnated by environmental friendly binder. It has good effect of thermal insulation with the characteristics of fiberuniformly dispersed,uniform thickness,low organic content,thermostability and low thermal conductivity. This producthas no corrosion effect to steel pipe due to the ultra low Cl-content. Well coated with the pipe,this product is applied tothe thermal insulation treatment of small diameter pipe.It is a new material for high temperature and high pressure thermalinsulation product.
Characteristic
. Fiber Uniformly Dispersed
. Smooth Surface,Uniform ThicknessSoft,Easy to Wind
. Low Thermal ConductivityThermostability,Less VOC
Packaging
1. Roll packaging: PE plastic film
2. Pallet packaging: Pallets should NOT be stacked in more than 2 layers.
Storage
This product should be stored in a dry, ventilated and rainproof place,with temperatures from 5℃to 35℃ and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.
Fiberglass Thermal Insulation Tissue
Technical Data
Product Code | Unit Weight (g/m2) | LOI (%) | MD Tensile Strength (N/50mm) | CD Tensile Strength (N/50mm) | Thickness(mm) | Moisture Content (%) |
BW200 | 200 | 8.0 | ≥280 | ≥140 | 2.0 | ≤1.0 |
BW300 | 300 | 8.0 | ≥350 | ≥200 | 3.0 | ≤1.0 |
BW400 | 400 | 8.0 | ≥420 | ≥250 | 4.0 | ≤1.0 |
Testing Basis | ISO 3374 | ISO 1887 | ISO 3342 | ISO 3342 | ISO4603@0.5KPa | ISO 3344 |
Paper core diameter: 76/152mm
Remark:
1. Any special products can also supply according to customers' request
2. The technical data above is for reference only
Description
Fiberglass thermal insulation tissue is made of E chopped fiber glass with wet laid process and cured at high
temperature after impregnated by environmental friendly binder. It has good effect of thermal insulation with the characteristics of fiberuniformly dispersed,uniform thickness,low organic content,thermostability and low thermal conductivity. This producthas no corrosion effect to steel pipe due to the ultra low Cl-content. Well coated with the pipe,this product is applied tothe thermal insulation treatment of small diameter pipe.It is a new material for high temperature and high pressure thermalinsulation product.
Characteristic
. Fiber Uniformly Dispersed
. Smooth Surface,Uniform ThicknessSoft,Easy to Wind
. Low Thermal ConductivityThermostability,Less VOC
Packaging
1. Roll packaging: PE plastic film
2. Pallet packaging: Pallets should NOT be stacked in more than 2 layers.
Storage
This product should be stored in a dry, ventilated and rainproof place,with temperatures from 5℃to 35℃ and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.