Fiberglass Battery Separator Tissue
Technical Data
Product Code | Unit Weight (g/m2) | LOI (%) | MD Tensile Strength (N/50mm) | Potassium Permanganate Content(ml/g) | Thickness (mm) | Moisture Content (%) |
GB0.3 | 30 | ≤20 | ≥70 | ≤15 | 0.30±0.03 | ≤1.0 |
GB0.5 | 55 | ≤20 | ≥110 | ≤15 | 0.50±0.04 | ≤1.0 |
GB0.7 | 80 | ≤20 | ≥130 | ≤15 | 0.70±0.04 | ≤1.0 |
GB0.8 | 105 | ≤20 | ≥180 | ≤15 | 0.80±0.05 | ≤1.0 |
Testing Basis | ISO 3374 | ISO 1887 | ISO 3342 | JB/T7630.1-20086.14 | ISO4603 | ISO 3344 |
Paper core diameter: 76/152mm
Remark:
1. Any special products can also supply according to customers' request
2. The technical data above is for reference only
Description
Fiberglass Battery Separator Tissue is a material with the property of good fiber dispersion,uniform thickness, potassiumpermanganate reducing content,low content of Cl- ,Fe³*and other trace elements and acid penetrating fast.The batterymade of fiberglass tissue has high starting current,excellent anti vibration performance,slow battery power attenuationand long service life.
Characteristic
. Smooth Surface,Uniform Thickness
. Good Acid Liquor Absorption Ability,
. Good Acid Resistance,Moderate Stiffness
. Low Potassium Permanganate Content
. Low Trace Element Content
Packaging
1. Roll packaging: PE plastic film
2. Pallet packaging: Pallets should NOT be stacked in more than 2 layers.
Storage
This product should be stored in a dry, ventilated and rainproof place,with temperatures from 5℃to 35℃ and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.
Fiberglass Battery Separator Tissue
Technical Data
Product Code | Unit Weight (g/m2) | LOI (%) | MD Tensile Strength (N/50mm) | Potassium Permanganate Content(ml/g) | Thickness (mm) | Moisture Content (%) |
GB0.3 | 30 | ≤20 | ≥70 | ≤15 | 0.30±0.03 | ≤1.0 |
GB0.5 | 55 | ≤20 | ≥110 | ≤15 | 0.50±0.04 | ≤1.0 |
GB0.7 | 80 | ≤20 | ≥130 | ≤15 | 0.70±0.04 | ≤1.0 |
GB0.8 | 105 | ≤20 | ≥180 | ≤15 | 0.80±0.05 | ≤1.0 |
Testing Basis | ISO 3374 | ISO 1887 | ISO 3342 | JB/T7630.1-20086.14 | ISO4603 | ISO 3344 |
Paper core diameter: 76/152mm
Remark:
1. Any special products can also supply according to customers' request
2. The technical data above is for reference only
Description
Fiberglass Battery Separator Tissue is a material with the property of good fiber dispersion,uniform thickness, potassiumpermanganate reducing content,low content of Cl- ,Fe³*and other trace elements and acid penetrating fast.The batterymade of fiberglass tissue has high starting current,excellent anti vibration performance,slow battery power attenuationand long service life.
Characteristic
. Smooth Surface,Uniform Thickness
. Good Acid Liquor Absorption Ability,
. Good Acid Resistance,Moderate Stiffness
. Low Potassium Permanganate Content
. Low Trace Element Content
Packaging
1. Roll packaging: PE plastic film
2. Pallet packaging: Pallets should NOT be stacked in more than 2 layers.
Storage
This product should be stored in a dry, ventilated and rainproof place,with temperatures from 5℃to 35℃ and humidity between 35% and 65%. It is recommended to be kept in intact package when not used to avoid damp.