Fiberglass Coated Thermal Insulation Board Facing Tissue
Technical Data
Product Code | Unit Weight (g/m2) | MD Tensile Strength (N/50mm) | CDTensile Strength (N/50mm) | Thickness (mm) | Moisture Content(%) |
TMC120S | 120 | ≥ 240 | ≥ 150 | 0.45+0.10 | ≤1.0 |
TMC140S | 140 | ≥ 260 | ≥ 170 | 0.45+0.10 | ≤1.0 |
TMC160S | 160 | ≥ 280 | ≥ 200 | 0.45+0.10 | ≤1.0 |
TMC180S | 180 | ≥ 300 | ≥ 210 | 0.45+0.10 | ≤1.0 |
TMC200S | 200 | ≥ 320 | ≥ 220 | 0.45+0.10 | ≤1.0 |
TMC240S | 240 | ≥ 350 | ≥ 240 | 0.45+0.10 | ≤1.0 |
TMC300S | 300 | ≥ 380 | ≥ 280 | 0.60+0.10 | ≤1.0 |
TMC350S | 350 | ≥ 400 | ≥ 280 | 0.60+0.10 | ≤1.0 |
TMC390S | 390 | ≥ 450 | ≥ 330 | 0.60+0.10 | ≤1.0 |
TMC430S | 430 | ≥ 500 | ≥ 350 | 0.80+0.10 | ≤1.0 |
TMC480S | 480 | ≥ 550 | ≥ 380 | 1.0+0.20 | ≤1.0 |
Testing basis | ISO 3374 | ISO 3342 | ISO4603@0.5Kpa | ISO3344 | |
Paper core diameter: 152/305mm
Remark:
1. Any special products can also supply according to customers' request
2. The technical data above is for reference only
Description
Fiberglass coated thermal insulation board facing tissue is applied as a facing layer to insulation boards with core materials such as mineral wool, glass wool, rock wool, PU, PIR, XPS, etc. It exhibits high adhesion strength with the core material, resulting in high bending resistance and exceptional compressive strength. The fiberglass coating facing felt for insulation boards finds wide applications in the construction industry, especially for exterior wall insulation, interior wall insulation, roof insulation, and partition filling insulation in residential buildings, apartments, hotels, office buildings, factories, warehouses, supermarkets, and more. It offers excellent insulation, fire resistance, water resistance, durability, and does not mold, wrinkle, or crack. It is an energy-efficient and environmentally friendly high-performance material.
Characteristic
. Uniform fiber dispersion and a smooth and dense felt surface
. Excellent water resistance and high strength retention
. Outstanding adhesion with core materials
. High compressive and bending strength
. Flame resistance, water resistance, no mold, no wrinkles