MS700
Howell
HM-MS700
Translucent High Tensile Strength MS Hybrid Sealant
Translucent Bonding and Sealing MS700 sealant is a high-quality, one-component MS polymer sealant with high tensile strength. This environment-friendly, low VOC adhesive offers exceptional bonding, durability, and flexibility, making it perfect for structural applications and a wide range of sealing needs.
◆High-grade aluminum profile door and window sealing
◆Marble curtain wall bonding and caulking
◆Aluminum plastic panel curtain wall bonding and caulking
◆Building interior decoration
◆Bonding and sealing of automobiles, ships, elevators, cold storage, etc.
Code# | MS700 |
Shelf Life | 12months |
Properties Uncured | |
Skin forming time (min)23 °C | 50 % r.h | 20 |
Density (g/cm3) | 1.05 |
Consistency | non-sag |
Properties Cured | |
Hardness (Shore A) | 34 |
Elongation at break (%) | 300 |
Tensile strength (N/mm2) | 2.0 |
Sealant grade | 20HM |
The above data is tested at 25℃ and 50% relative humidity. After cured for 21 days at a humidity of 50±5% and a temperature of 23±2℃ Standard colors are white, black, gray, and transparent. Other colors can be provided according to customer needs. |
Construction:
Cut the branch opening, put on the glue nozzle, cut the glue nozzle into a suitable slope, and apply it tothe construction site with a glue extrusion gun. During pneumatic gluing, the air pressure isrecommended not to exceed 0.4 MPa, and the construction temperature is recommended to be 4°C -40°C
Curing:
Place the glued parts in the air. After the skin is formed, it will cure from the surface to the inside. Thecuring depth will be 2~4mm within 24 hours at room temperature and 55% relative humidity. As timegoes by, the curing depth gradually increases.
Storage:
Unused glue should be tightened immediately and the nozzle should be sealed for storage. When usingit again, if there is a little crust on the seal, just remove it and it will not affect normal use. During thestorage process, a small amount of crusting may also appear on the branch mouth. After removal, it canbe used normally without affecting product performance.
Standard 300ml plastic bottle packing, 24pcs/carton;
500-600ml flexible film packing, 20pcs/carton
Store the original sealant in a dry place, the temperature should not be higher than 27 °C, and the storageperiod is 12 months from the date of production
HM-MS700
Translucent High Tensile Strength MS Hybrid Sealant
Translucent Bonding and Sealing MS700 sealant is a high-quality, one-component MS polymer sealant with high tensile strength. This environment-friendly, low VOC adhesive offers exceptional bonding, durability, and flexibility, making it perfect for structural applications and a wide range of sealing needs.
◆High-grade aluminum profile door and window sealing
◆Marble curtain wall bonding and caulking
◆Aluminum plastic panel curtain wall bonding and caulking
◆Building interior decoration
◆Bonding and sealing of automobiles, ships, elevators, cold storage, etc.
Code# | MS700 |
Shelf Life | 12months |
Properties Uncured | |
Skin forming time (min)23 °C | 50 % r.h | 20 |
Density (g/cm3) | 1.05 |
Consistency | non-sag |
Properties Cured | |
Hardness (Shore A) | 34 |
Elongation at break (%) | 300 |
Tensile strength (N/mm2) | 2.0 |
Sealant grade | 20HM |
The above data is tested at 25℃ and 50% relative humidity. After cured for 21 days at a humidity of 50±5% and a temperature of 23±2℃ Standard colors are white, black, gray, and transparent. Other colors can be provided according to customer needs. |
Construction:
Cut the branch opening, put on the glue nozzle, cut the glue nozzle into a suitable slope, and apply it tothe construction site with a glue extrusion gun. During pneumatic gluing, the air pressure isrecommended not to exceed 0.4 MPa, and the construction temperature is recommended to be 4°C -40°C
Curing:
Place the glued parts in the air. After the skin is formed, it will cure from the surface to the inside. Thecuring depth will be 2~4mm within 24 hours at room temperature and 55% relative humidity. As timegoes by, the curing depth gradually increases.
Storage:
Unused glue should be tightened immediately and the nozzle should be sealed for storage. When usingit again, if there is a little crust on the seal, just remove it and it will not affect normal use. During thestorage process, a small amount of crusting may also appear on the branch mouth. After removal, it canbe used normally without affecting product performance.
Standard 300ml plastic bottle packing, 24pcs/carton;
500-600ml flexible film packing, 20pcs/carton
Store the original sealant in a dry place, the temperature should not be higher than 27 °C, and the storageperiod is 12 months from the date of production
Anti-mildew | Aquarium | Automobile | Construction Exterior Wall | Decoration | Electronics | Elevator | Farbricated Building | Home Appliances | Infrastructure | Nail Free | Pipe Thread Locking | Planar Sealing | Rail Traffic | Screw-locking | Silicone Conformal Coatings | Universal | Waterproof | Windows&Sun Romms